Product Details:
Payment & Shipping Terms:
|
Diameter(mm):: | Φ0.96mm | Tensile Strength (Mpa):: | 1920-2100 |
---|---|---|---|
Yield Ratio (%):: | 92.7-93.9 | Elongation At Break (%): | 7.2 -8.8 |
Tensile Strength (Mpa): | 1920-2100 | Yield Ratio(%): | 92.7-93.9 |
Bronze Coated(g/kg): | 0.40-0.52 | Cu(%): | 98.3-99.2 |
Application: | Automobiles, Bicycle, Bike, Motorcycles, Planes, Vehicles | Feature: | Bronze Coated, Durable, Normal Tensile, Rustproof, Waterproof |
High Light: | low carbon steel rod,carbon steel wire rod,tensile strength of low carbon steel |
Rustproof Φ0.96mm Bronze Coated Low Carbon Steel Wire For Vehicles
2100mpa tensile strength
Copper coated smoothly
6000MT monthly production
Description:
Bead wire for tire rim is widely applied to the manufacturing of various tires rims for automobiles,motorcycles,planes as well as other vehicles.It’s the pivotal material of tire,which can strengthen the tire and is considered an important raw material for the tyre manufacturing business.
Specifications:
Description |
BEAD WIRE |
Reference |
GB/T14450- 2008 |
Diameter |
Φ0.96mm |
||||
Item |
Standard |
Result |
|||||||
Diameter(mm) |
0.96±0.02 |
0.94-0.97 |
|||||||
Tensile strength (Mpa) |
≥1850 |
1920-2100 |
|||||||
Yield ratio (%) |
92.0-95.0 |
92.7-93.9 |
|||||||
Elongation at break (%) |
≥5 |
7.2 -8.8 |
|||||||
Torsion (360°/200d) |
≥28 |
30-40 |
|||||||
Residual torsion (°/9m) |
≯360 |
90-120 |
|||||||
Bronze coated(g/kg) |
0.35-0.65 |
0.40-0.52 |
|||||||
Cu (%) |
≥97 |
98.3-99.2 |
|||||||
Sn (%) |
0.5-3.0 |
0.80-1.70 |
|||||||
Straightness (mm/3m) |
≤400 |
120-400 |
|||||||
Adhesion (N/50mm) |
≥932 |
1255 |
|||||||
Surface Quality |
Coating Smooth and uniform |
conform |
|||||||
Assay of chemical contents |
|||||||||
C |
Mn |
Si |
P |
S |
|||||
0.70-0.72 |
0.50-0.60 |
0.17-0.30 |
0.006-0.016 |
0.005-0.018 |