Product Details:
Payment & Shipping Terms:
|
Diameter(mm):: | Φ 1.20mm | Elongation At Break (%): | 5.0-6.0 |
---|---|---|---|
Torsion(360°/100d): | 29-35 | Breaking Force (Mpa): | 1800-1860 |
Yield Ratio(%): | 85.4-87.6 | Bronze Coated(g/kg): | 0.32-0.36 |
Cu(%): | 98.3 | Application: | Automobiles, Bicycle, Bike, Motorcycles, Planes, Vehicles |
Feature: | Bronze Coated, Durable, Rustproof | ||
High Light: | low carbon steel rod,carbon steel wire rod,tensile strength of low carbon steel |
Φ1.2mm Bronze Low Coated Rustproof Carbon Steel Wire For Tire Bead Wire
First-class material
High tensile 2250mpa
Elongation at break 6.0%
Description:
Bead wire for tire rim is widely applied to the manufacturing of various tires rims for automobiles,motorcycles,planes as well as other vehicles.It’s the pivotal material of tire,which can strengthen the tire and is considered an important raw material for the tyre manufacturing business.
Specifications:
Description |
BEAD WIRE |
Reference |
GB/T14450- 2008 |
Diameter |
Φ 1.20mm |
Item |
Standard |
Result |
|||
Diameter(mm) |
1.17-1.20 |
1.17-1.20 |
|||
Breaking force (Mpa) |
≥1800 |
1800-1860 |
|||
Elongation at break(%) |
≥5.0 |
5.0-6.0 |
|||
Yield ratio(%) |
≥80 |
85.4-87.6 |
|||
Torsion(360°/100d) |
≥26 |
29-35 |
|||
Bronze coated(g/kg) |
0.30-0.65 |
0.32-0.36 |
|||
Sn (%) |
0.3-3.0 |
1.7 |
|||
Cu(%) |
≥97 |
98.3 |
|||
Straightness(mm/3m) |
≤600 |
200-500 |
|||
Surface Quality |
Coating Smooth and uniform |
conform |