Product Details:
Payment & Shipping Terms:
|
Diameter(mm):: | Φ 1.20mmHT | Elongation At Break (%): | 5.0-6.0 |
---|---|---|---|
Torsion(360°/100d): | 29-35 | Breaking Force (Mpa): | 2150-2250 |
Yield Ratio(%): | 85.4-87.6 | Bronze Coated(g/kg): | 0.32-0.36 |
Cu(%): | 98.3 | Application: | Automobiles, Bicycle, Bike, Motorcycles, Planes, Vehicles |
Feature: | Bronze Coated, Durable, High Tensile, Rustproof | ||
High Light: | mild steel wire,copper clad steel wire,low carbon steel rod |
Cu 98.3% Coated Low Carbon Steel Wire For Tire Bead Wire
2250mpa high tensile strength
Cu 98.3% coated smoothly
Multiple payment
Description:
Bead wire for tire rim is widely applied to the manufacturing of various tires rims for automobiles,motorcycles,planes as well as other vehicles.It’s the pivotal material of tire,which can strengthen the tire and is considered an important raw material for the tyre manufacturing business.
Specifications:
Description |
BEAD WIRE |
Reference |
GB/T14450- 2008 |
Diameter |
Φ 1.20mmHT |
Item |
Standard |
Result |
|||
Diameter(mm) |
1.17-1.20 |
1.17-1.20 |
|||
Breaking force (Mpa) |
≥2100 |
2150-2250 |
|||
Elongation at break(%) |
≥5.0 |
5.0-6.0 |
|||
Yield ratio(%) |
≥80 |
85.4-87.6 |
|||
Torsion(360°/100d) |
≥26 |
29-35 |
|||
Bronze coated(g/kg) |
0.30-0.65 |
0..32-0.36 |
|||
Sn (%) |
0.3-3.0 |
1.7 |
|||
Cu(%) |
≥97 |
98.3 |
|||
Straightness(mm/3m) |
≤600 |
200-500 |
|||
Surface Quality |
Coating Smooth and uniform |
conform |