Product Details:
Payment & Shipping Terms:
|
Diameter(mm):: | Φ 1.8mm | Elongation At Break (%): | 5.0-6.0 |
---|---|---|---|
Torsion(360°/100d): | 29-35 | Breaking Force (Mpa): | 1800-1860 |
Yield Ratio(%): | 85.4-87.6 | Bronze Coated(g/kg): | 0.32-0.36 |
Diameter(mm): | 1.78-1.82 | Cu(%): | 98.3 |
Application: | Automobiles, Bicycle, Bike, Motorcycles, Planes, Vehicles | Feature: | Bronze Coated, Durable, Normal Tensile, Rustproof, Waterproof |
High Light: | mild steel wire,copper clad steel wire,low carbon steel rod |
Automobiles Tire Low Carbon Steel Wire , 1860Mpa Breaking Force
Colour and lustre is bright
Superior quality with high material
Breaking force 1860Mpa
Description:
Bead wire for tire rim is widely applied to the manufacturing of various tires rims for automobiles,motorcycles,planes as well as other vehicles.It’s the pivotal material of tire,which can strengthen the tire and is considered an important raw material for the tyre manufacturing business.
Specifications:
Description |
BEAD WIRE |
Reference |
GB/T14450- 2008 |
Diameter |
Φ 1.8mm |
Item |
Standard |
Result |
|||
Diameter(mm) |
1.8± 0.02 |
1.78-1.82 |
|||
Breaking force (Mpa) |
≥1800 |
1800-1860 |
|||
Elongation at break(%) |
≥5.0 |
5.0-6.0 |
|||
Yield ratio(%) |
≥85 |
85.4-87.6 |
|||
Torsion(360°/100d) |
≥25 |
29-35 |
|||
Bronze coated(g/kg) |
0.20-0.40 |
0.32-0.36 |
|||
Sn (%) |
0.3-3.0 |
1.7 |
|||
Cu(%) |
≥97 |
98.3 |
|||
Surface Quality |
Coating Smooth and uniform |
conform |