Diameter(mm):: | Φ 1.83mmHT | Yield Ratio (%):: | 85.4-87.6 |
---|---|---|---|
Elongation At Break (%): | 5.0-6.0 | Torsion(360°/100d): | 29-35 |
Breaking Force (Mpa): | 2050-2200 | Yield Ratio(%): | 85.4-87.6 |
Bronze Coated(g/kg): | 0.32-0.36 | Cu(%): | 98.3 |
Application: | Automobiles, Bicycle, Bike, Motorcycles, Planes, Vehicles | Feature: | Bronze Coated, Durable, High Tensile, Rustproof, Waterproof |
High Light: | mild steel wire,copper clad steel wire,low carbon steel rod |
High Tensile Φ1.83mm Carbon Steel Wire , Brass Plated Steel Wire
2200mpa high tensile strength
Coil with Six steel belts fixed
6000MT monthly production
Description:
Bead wire for tire rim is widely applied to the manufacturing of various tires rims for automobiles,motorcycles,planes as well as other vehicles.It’s the pivotal material of tire,which can strengthen the tire and is considered an important raw material for the tyre manufacturing business.
Specifications:
Description |
BEAD WIRE |
Reference |
GB/T14450- 2008 |
Diameter |
Φ 1.83mmHT |
Item |
Standard |
Result |
|||
Diameter(mm) |
1.83± 0.02 |
1.81-1.85 |
|||
Breaking force (Mpa) |
≥2050 |
2050-2200 |
|||
Elongation at break(%) |
≥5.0 |
5.0-6.0 |
|||
Yield ratio(%) |
≥85 |
85.4-87.6 |
|||
Torsion(360°/100d) |
≥25 |
29-35 |
|||
Bronze coated(g/kg) |
0.20-0.40 |
0.32-0.36 |
|||
Sn (%) |
0.3-3.0 |
1.7 |
|||
Cu(%) |
≥97 |
98.3 |
|||
Surface Quality |
Coating Smooth and uniform |
conform |